Structural evolution during mechanical alloying and subsequent annealing of high-entropy AlCuNiFeTi alloy

Скорочена інформація про документ
dc.contributor.authorYurkova, Alexandra Ivanovna
dc.contributor.authorChernyavsky, Vadym
dc.contributor.authorScheretskiy, Oleksandr
dc.date.accessioned2016-06-06T08:56:44Z
dc.date.available2016-06-06T08:56:44Z
dc.date.issued2015
dc.description.abstractenThis study reports the structural evolution of equiatomic AlCuNiFeTi high-entropy alloy (HEA) from elemental materials to solid solution during mechanical alloying (MA), and further, to equilibrium phases during subsequent thermal annealing. It was justified experimentally that MA of Al-Cu-Ni-Fe-Ti powder mixture during 15 hours resulted in a single-phase nanocrystalline HEA with a structure of ВCC solid solution. During thermal annealing recovery and recrystallization of the BCC solid solution take place at temperatures ranging from 130 to 650 °C, and phase transformation, and grain growth of equilibrium phases occur at higher temperatures. The phase composition transforms to BCC and FCC solid solutions when the MA powder was annealed at 700 °C for 1 h. The BCC and FCC solid solution structure can be maintained even after the alloy was annealed at 1000 °C. The alloy powder was consolidated by pressure sintering at 800 °C with 5 GPa pressure for half an hour. The sintered sample exhibits 10.7±0.3 GPa in Vickers hardness.uk
dc.format.pagerangePp. 32-35uk
dc.identifier.citationYurkova, A. Structural evolution during mechanical alloying and subsequent annealing of high-entropy AlCuNiFeTi alloy / А. Yurkova, V. Chernyavsky, O. Scheretskiy // Material Scince. Nonequilibrium Phase Tranformation. – 2015. – №1. – P. 32-35uk
dc.identifier.urihttps://ela.kpi.ua/handle/123456789/16189
dc.language.isoenuk
dc.publisherScientific technical union of mechanical engineeringuk
dc.publisher.placeSofiauk
dc.publisher.placeBulgariauk
dc.source.nameInternational Journal Material Scince. Nonequilibrium Phase Tranformationuk
dc.status.pubpublisheduk
dc.subjectHigh-entropy alloyuk
dc.subjectmechanical alloyinguk
dc.subjectstructural evolutionuk
dc.subjectphase compositionuk
dc.subjectannealinguk
dc.subjectmechanical propertiesuk
dc.titleStructural evolution during mechanical alloying and subsequent annealing of high-entropy AlCuNiFeTi alloyuk
dc.typeArticleuk

Файли

Контейнер файлів
Зараз показуємо 1 - 1 з 1
Ескіз
Назва:
Material Scince. Nonequilibrium Phase Tranformation. – 2015. – №. 1. – P. 32-35.pdf
Розмір:
624.6 KB
Формат:
Adobe Portable Document Format
Завантажити
Ліцензійна угода
Зараз показуємо 1 - 1 з 1
Ескіз недоступний
Назва:
license.txt
Розмір:
7.71 KB
Формат:
Item-specific license agreed upon to submission
Опис:
Завантажити

Зібрання

Статті (ВМПМ ІФФ)