Перегляд за Автор "Loboda, P. I."
Зараз показуємо 1 - 12 з 12
Результатів на сторінці
Налаштування сортування
Документ Відкритий доступ Effect of Molybdenum Additions on the Microstructure and Properties of WC-W2C Alloys(Springer Nature, 2014-07) Trosnikova, I. Y.; Loboda, P. I.; Bilyi, O. I.The paper examines how additions of 5, 10, and 20 wt.% molybdenum influence the structure, stress–strain state, phase composition, and size of phase components in WC–W2C alloys. It is found that 5 wt.% molybdenum leads to 30% increase in the microhardness and twofold to threefold increase in the wear resistance of cast tungsten carbide compared to the alloy without additions. Higher molybdenum content of the WC–W2C alloys changes the phase composition and increases compressive stresses in the W2C matrix phase and tensile stresses in WC, (Mo, W)2C, and Mo2C inclusions.Документ Відкритий доступ Effect of Plating of Carbon Fibres with Ni on Properties of Fe-Based Materials(Nanosistemi, Nanomateriali, Nanotehnologii, Т. 20, № 4, 2022) Elkady, Mahmud; Minitsky, A. V.; Trosnikova, I. Yu.; Loboda, P. I.; Leonov, D. S.У роботі досліджено формування структури та властивості матеріалу на основі карбонільного заліза, армованого вуглецевими волокнами, попередньо плакованими нікелем. Для першої партії зразків було застосовано неплаковані вуглецеві волокна, а для другої — вуглецеві волокна, плаковані нікелем. Встановлено, що плакування нікелем забезпечує кращу адгезійну взаємодію між вуглецевими волокнами та залізом. Показано, що армування вуглецевими волокнами, плакованими нікелем, уможливлює збільшити як границю міцності, так і пластичність матеріалів. Для зразків, спечених за 900С, міцність зростає непринципово — від 661 МПа до 697 МПа, однак відносне видовження збільшується вдвічі — від 22,7% до 45,1%. Методом фрактографічної аналізи встановлено в’язкий характер руйнування зразків і показано, що мікрорельєф поверхні характеризується косими зламами, що зумовлено утворенням в’язких ямок під дією дотичних напружень. Збільшення температури спікання до 1000С забезпечує зростання міцності на стиснення зразків до 1002–1185 МПа; зразки, які містять плаковані волокна, мають міцність, на 180–185 МПа вищу за міцність зразків з вуглецевими волокнами, неплакованими нікелем.Документ Відкритий доступ Effect of the cooling rate during melt solidification on the structure and properties of WC-W2C(Springer Nature, 2014) Trosnikova, I. Yu.; Loboda, P. I.; Karasevska, O. P.; Bilyi, O. I.By optical and scanning electron microscopy and quantitative X-ray diffraction and X-ray analysis revealed that the increase in the rate of cooling during crystallization from the melt leads to a reduction in the size of the phase components of the alloy of 20 wt.% WC-80 wt.% W2C, increased compressive stress in the matrix phase W2C and stretching inclusions in the WC, which leads to an increase in the hardness of 1.5 times and 2-4 times the strength of relit, that is used on an industrial scale for the strengthening of machine parts and mechanisms operating in abrasive wear and high contact loads.Документ Відкритий доступ Influence of Obtaining Conditions on Microstructure, Phase Composition and Properties of Eutectic Alloy of WC–W2C System(Allerton Press, Inc., 2019) Trosnikova, I. Yu.; Loboda, P. I.Документ Відкритий доступ Optimization of the sintering parameters for materials manufactured by powder injection molding(Springer Nature, 2020) Zavadiuk, S. V.; Loboda, P. I.; Soloviova, T. O.; Trosnikova, I. Yu.; Karasevska, O. P.Документ Відкритий доступ Structural regularities of welded seam between Ti-Tib and vanadium with 12X18H10T interlayer by using electron beam welding(Igor Sikorsky Kyiv Polytechnic Institute, 2020) Loboda, P. I.; Zvorykin, C. O.; Zvorykin, V. L.; Vrzhyzhevskyi, E. L.; Taranova, T. G.; Kostin, V. A.Документ Відкритий доступ The structure and properties of the molybdenum-doped WC–W2C eutectic alloy depending on the production method(Springer Nature, 2019) Trosnikova, I. Yu.; Loboda, P. I.; Karasevska, O. P.Документ Відкритий доступ Вплив кінетичних параметрів процесу кристалізації на структуру та властивості евтектичного сплаву системи LaB6-TiB2(2016-05) Лобода, П. І.; Соловйова, Т. О.; Богомол, Ю. І.; Ремізов, Д. О.; Білий, О. І.; Loboda, P. I.; Soloviova, T. O.; Bogomol, Y. I.; Remizov, D. O.; Bilyi, O. I.; ВТМ та ПМ; ІФФ; НТУУ «КПІ»Документ Відкритий доступ Вплив механічних коливань на формування мікроструктури монокристалів і керамічних композитів під час вирощування з розплаву(НТУУ "КПІ", 2013) Лобода, П. І.; Богомол, Ю. І.; Соловйова, Т. О.; Loboda, P. I.; Bogomol, Yu. I.; Solovyova, T. O.; Лобода, П. И.; Богомол, Ю. И.; Соловьева, Т. А.Документ Відкритий доступ Створення фізико-хімічних основ керування ультратонкою структурою квазів'язкої армованої високотемпературної кераміки поліфункціонального застосування(НТУУ «КПІ», 2012) Лобода, П. І.; Loboda, P. I.; Лобода, П. И.; Кафедра високотемпературних матеріалів та порошкової металургії; Інженерно-фізичний факультет; Національний технічний університет України «Київський політехнічний інститут»Документ Відкритий доступ Структура та властивості квазіпотрійних спрямовано армованих композитів системи В4С–TiB2–SiC(2016-05) Богомол, Ю. І.; Лобода, П. І.; Головенько, Я. Б.; Bogomol, I. I.; Loboda, P. I.; Holovenko, Ya. B.; Богомол, Ю. И.; Лобода, П. И.; Головенько, Я. Б.; ВТМ та ПМ; ІФФ; НТУУ "КПІ"Документ Відкритий доступ Структура і властивості спрямовано закристалізованого сплаву системи Mo-8,7 Si-18 В(НТУУ "КПІ", 2016) Богомол, Юрій Іванович; Попович, Ольга Ігорівна; Крюгер, Маня; Лобода, Петро Іванович; Bogomol, Y. I.; Poppvych, O. I.; Krueger, M.; Loboda, P. I.; Богомол, Ю. И.; Попович, О. И.; Крюгер, М.; Лобода, П. И.